Product Description

Hot Die Steel H -13 Aluminum Extrusion Ejector Cor

Steel Properties : High hot-wear resistance, high hot tensile strength and toughness. Good thermal conductivity and insusceptibility to hot cracking. Can be water-cooled to a limited extent.

Applications : Hot-work tool steel for universal use. Pressure casting dies and metal extrusion tools for processing light metals, forging dies, moulds, screws and barrels for plastic processing, nitrided ejectors, hot-shear blades. Suitable for Aluminium Extrusion Die & Aluminium Copper Forging Dies.

H13 has high hard resistance and hardness. Suitable for Aluminium Extrusion Die, and Aluminium Copper forging Die.

TG Premium Quality Hot Work Tool Steel
1. TGPH13 : Special for Aluminum - Magnesium alloy compression mold & core rod
2. TGH13W (patented grade) : Special for Aluminium Allow extrusion mold & hot forged die & compression mold


Similar steel grade

BRAZIL

AUSTRIA

GERMANY

SLOVANIA

ITALY

JAPAN

S.KORIA
TAIWAN

CHEZ. REP

VILLARES

BOHLER

DEW

GRODITZ

RAVNE

LUCCHINI

HITACHI

NIPPON
SANYO
DOOSAN
GLORIA

POLDI

VH13IM
W302
1.2344
1.2344
UTOP M02-EFS
ESKY0S2344
DAC
KDA
QD61
STD 61
GMH13 (ESR)
TLI EFS


Chemical Composition: (%) 

Indian
Chemical Analysis Typical Value % (Min - Max)
Delivery Condition
IS
C
S
P
Si
Mn
Ni
Cr
Mo
V
W
other
Heat
Treatment
Hardness
XT8W6M05Cr4V2
0.38-
0.45
<0.030
<0.030
0.80-
1.20
0.25-
0.50
***
4.80-
5.50
1.20-
1.50
0.85-
1.15
***
***
Annealed
HB235
TGPH13
0.38
Max
0.005
Max
0.002
1
0.3
***
5
1
1
***
***
1010-1050
40-50
TGH13W
Cr-W-Mo-V Alloy Steel, improved on H13, patented grade
1010-1050
41-52


Production process:

Round Bar :

EAFLFVDESR(5TONS HAMMER)   (FORGED & TURNED) - 81.0-610.0mm  
(HOT ROLLED & PEELED) - 14.5-80.0mm ANNEALED CONDITION
  (COLD GROUND) - 4.5-14.4mm  

Flat Bar :

EAF LF VD ESR FORGED HOT ROLLED (850) ANNEALED CONDITION


UT standard : REDUCTION RATIO : DELIVERY STATUS :
SEP 1921, (DEC.84)E/e As 1:4 or 1:5 In Annealed Condition.


Size : Round

Cold Drawn/Ground Bar
Hot Rolled Annealed & Peeled Bar
Forged + Annealed + Turned Bar
4.5 - 14.4mm
14.5 - 80.0mm
81.0 - 610.0mm

Size : Hot Rolled Flat Bars / Sand Blasted & Machined Straight

Thickness
Width
14mm - 100mm
100mm - 810mm


Heat Treatment Condition :
Quenching temperature : 1020-1050℃
Cooling Medium : air-cooling
Tempering temperature : 550-650℃
Tempering times : 2Times, the tempering temperature in the second time should be lower than in first time
Tempering Hardness : 47-48HRC.

 
Tempering°C
500°C
550°C
600°C
HRC
HRC56
HRC54
HRC50

 


TGK SPECIAL STEEL PVT. LTD.